For the corrosion protection of battery trucks, we must first understand the causes of corrosion

The competition in the electric hydraulic truck market is fierce, and the storage pallet truck manufacturers have also made great efforts to explore the merits of battery trucks in terms of sales. Among them, the anti-corrosion technology is also a point that needs to be worked hard, so that it can be favored by customers in appearance, and the service life of the pallet truck can be effectively extended, so that the quality of the equipment can be effectively improved. It can even become a major buying point for the product. Let's take a look at the main factors that cause the corrosion of the truck.

Environmental factors that cause corrosion of electric hydraulic trucks

When it comes to environmental factors, we often mention the places where battery trucks are used, such as ports, seaports, and industrial and mining sites. In such a special environment, the mineral dust and waste liquid in the environment will cause certain corrosion to the shell of the equipment. Secondly, man-made or weather is also a factor to be concerned about. For example, some port areas will be affected by tropical, humid tropical and marine climates, and the moisture in the atmosphere will also cause corrosion and damage to equipment components. Equipment used in warehouses and other indoor places is not greatly affected by the environment, and the corrosion caused by environmental factors is relatively light.

The structural factors that cause the corrosion of the electric hydraulic truck

The acid mist and liquid leakage generated when the battery is running when the electric hydraulic truck is in use Some damage caused by the action of vibration and impact is also the cause of corrosion and damage to equipment parts. Steel corrosion is a metal corrosion product that is converted into metal corrosion under the influence of the environment, which causes the accessories to rust and damage.

The corrosion of non-metallic materials such as paint film, rubber and ABS is affected by the environment, and the macromolecular structure of the material undergoes physical changes and qualitative changes, resulting in an unsightly appearance and some functions will be reduced. From this, it can be seen that the appearance and structure of the battery truck itself, the use of materials, the forging process, and the anti-corrosion method will indirectly affect the quality of the equipment.